Material number: 1202

Thickness ISO 1183 1,39 g/cm3

Mechanical Properties

• Extensional Strain ISO 527 65 MPa
• Ultimate ElongationISO 527 27 %
• Zug-E-Modul ISO 527 2700 MPa
• Ball pressure hardness ISO 2039-1 145 MPa
• Norm for Ball pressure hardness H358/30
• Hardness Shore (A/D) or Rockwell (R/L/M) ISO 868, ISO 2039-2 D81
• Izod-notched impact strength at 23 °C (73.4 ° F) ISO 180/1A 5,5 KJ/m2
• Charpy-notched impact strength at 23 °C  (73.4 ° F) ISO 179/1eA 6,0 KJ/m2

Electrical Properties

• Relative permittivity at 50 Hz IEC 60250 3,8 -
• Relative permittivity at 1 MHz IEC 60250 3,8 -
• Dielectric loss factor at 50 Hz IEC 60250 10 1E-4
• Dielectric loss factor at 1 MHz IEC 60250 50 1E-4
• Dielectric strength IEC 60243-1 40 kV/mm
• Thickness for dielectric strength 1,0 mm
• Volume resistivity IEC 60093 1014 Ohm · m
• Surface resistivity IEC 60093 1014 Ohm
• Tracking current resistance CTI IEC 60112 600

Thermal Features

• Heat conductivity DIN 52 612 0,31 W/K m
• Linear expansion lengthwise|cross to flow direction ISO 11359 110 10-6/K
• Glaze or glass transition temperature ISO 11357 167 °C
• Warmth form resistance A ISO 75 HDT/A (1.8 MPa) 105 °C max.
• Temperature short term 140 °C max.
• Temperature constantly 100 °C min.
• Application temperature -50 °C